gain in weight

Inorganic material
A part of the sludge, 1.0 gram, was dissolved in 100 ml of Chloroform.
A 1.2 μm filter (Whatman, ME28, membrane filter, mixed cellulose ester) was weighed, and the organic fluid was filtered through this 1.2 μm filter. The filter was washed 3 times with 20 ml of Chloroform.
The 1.2 μm filter was again weighed after evaporation of the Chloroform, to determine the amount of insoluble material.
Calculations: Insoluble material in %: Gain in weight of 1.2 μm filter x 100 Weight of the organic fluid
A photo of the filter containing the inorganic material was taken and was analysed by FTIR. Organic material
The Chloroform is evaporated of the organic phase and analyzed by FT-IR too

Anorganisches material
 Ein Teil des Schlammes, 1,0 Gramm aufgelöst in 100 ml Chloroform.
 War ein 1,2 μm-Filter (Whatman, ME28, Membranfilter, gemischte Zellulose-Ester)
 gewogen, und die organische Flüssigkeit wurde durch diesen 1,2 μm-Filter gefiltert. Der filter
 wurde 3 Mal mit 20 ml Chloroform gewaschen.
 Der 1,2 μm-Filter wurde nach Verdampfung des Chloroform wieder zu abgewogen werden.
 bestimmen Sie die Menge an unlöslichen Material.
 Berechnungen:
 Unlöslichen Material in %: gewinnen an Gewicht von 1,2 μm-Filter X 100
 Gewicht der organische Flüssigkeit
 Ein Foto des Filters mit das anorganische Material wurde übernommen und war
 von FTIR analysiert.
 Organisches material
 Das Chloroform ist verdunstet der organischen Phase und auch von FT-IR analysiert